Base Material |
100% Polyester |
DIN 60001, ASTM D7641 |
Yarn |
75 D * 75 D |
DIN EN 2060, ASTM D1907 |
Weave Method |
Warp-knitted 2 bar |
-- |
Weight |
230 ± 10 gsm |
ISO536 |
Thickness |
510 ±50 μm |
ISO534 |
Opacity |
≥ 85% |
ISO2471 |
Color (Lab) |
L88.5 ±2; a8.5 ±2; b19.5 ±2 |
-- |
Gloss at 60° |
4 ±2 |
-- |
Elasticity |
Warp 10 ±3 %; Weft 12 ±3 % |
Length*Width=200*50mm Speed=100mm/min, Tension=20N |
Shrinkage |
≤ 2% |
200°C,45s |
Yellowing Delta E |
≤ 2 |
200°C,45s |
Flame Resistance |
DIN 4102-1 B1, NFPA 701 |
DIN 4102-1 B1, NFPA 701 |
Recommended Fixation Temperature |
374 — 392°F, 45s |
-- |
Yellowing Temperature |
≥410°F |
SUPRKC REX-C400, 30s |