TESSUTO Triple white, BACKLIT |
Base Material |
100% Polyester |
DIN 60001, ASTM D7641 |
Yarn |
300 D * 7s D |
DIN EN 2060, ASTM D1907 |
Weave Method |
Woven |
-- |
Weight |
250 ±10 gsm |
ISO536 |
Thickness |
470 ±50 μm |
ISO534 |
Opacity |
90 % ±5 |
ISO2471 |
Whiteness |
165 ±10 |
ISO 11475 |
Color (Lab) |
L91.5 ±2; a8 ±2; b-19 ±2 |
-- |
Gloss at 60° |
4 ±2 |
-- |
Elasticity |
3% ± 2 |
Length*Width=200*50mm Speed=100mm/min, Tension=20N |
Shrinkage |
≤ 2% |
200°C, 45s |
Yellowing Delta E |
≤ 2 |
200°C, 45s |
Flame Resistance |
DIN 4102-1 B1, NFPA 701 |
DIN 4102-1 B1, NFPA 701 |
Recommended Fixation Temperature |
190—200°C, 45s |
-- |
≥200°C, |
SUPRKC REX-C400, 30s |